Analytical Results of DWPF Glass Sample Taken During Pouring of Canister S01913

Bannochie, C

Savannah River Site (S.C.)

关键词: Sludges;    Chemical Composition;    Waste Forms;    Density;    36 Materials Science;   

DOI  :  10.2172/890153
RP-ID  :  WSRC-TR-2004-00316, Rev. 2
RP-ID  :  DE-AC09-96SR18500
RP-ID  :  890153

美国|英语

来源: UNT Digital Library

【 摘 要 】

The Defense Waste Processing Facility (DWPF) began processing Sludge Batch 2 (SB2) (Macrobatch 3) in December 2001 as part of Sludge Receipt and Adjustment Tank (SRAT) Batch 208. Macrobatch 3 consists of the contents of Tank 40 and Tank 8 in approximately equal proportions. A glass sample was obtained while pouring Canister S01913 and was sent to the Savannah River National Laboratory (SRNL) Shielded Cells for characterization. This report contains observations of the glass sample, results for the density, the chemical composition, the Product Consistency Test (PCT) and the radionuclide results needed for the Production Record for Canister S01913. The following conclusions are drawn from this work: (1) The glass sample taken during the filling of canister S01913 received at SRNL weighed 33.04 grams and was dark and reflective with no obvious inclusions indicating the glass was homogeneous. (2) The results of the composition for glass sample S01913 are in good agreement ({+-} 15%) with the DWPF SME results for Batch Number 254, the SME Batch that was being fed to the melter when the sample was collected. (3) The calculated WDF was 2.58. (4) Acid dissolution of the glass samples may not have completely dissolved the noble metals rhodium and ruthenium. (5) The PCT results for the glass (normalized boron release of 1.18 g/L) indicate that it is greater than seven standard deviations more durable than the EA glass; thus, the glass meets the waste acceptance criterion for durability. (6) The measured density of the glass was 2.56 {+-} 0.03 g/cm{sup 3}.