Weldability of Fe-Al-Cr Overlay Coatings for CorrosionProtection in Oxidizing/Sulfidizing Environments | |
Regina, JR | |
Oak Ridge National Laboratory | |
关键词: Corrosion; Aluminium; Boilers; Alloys; Testing; | |
DOI : 10.2172/885600 RP-ID : ORNL/SUB/95-SU604/05 RP-ID : DE-AC05-00OR22725 RP-ID : 885600 |
|
美国|英语 | |
来源: UNT Digital Library | |
【 摘 要 】
The effect of chromium additions to the weldability of Fe-Al based overlay claddings are currently being investigated for the corrosion protection of boiler tubes in Low NOx furnaces. The primary objective of this research is to identify weldable (crack-free) Fe-Al-Cr weld overlay coating compositions that provide corrosion resistance over long exposure times. During the current project phase, preliminary corrosion testing was conducted on several ternary Fe-Al-Cr alloys in two types of gaseous corrosion environments. These long-term corrosion tests were used to develop a target weld composition matrix and serve as a base line for future corrosion tests. Preliminary Fe-Al based welds with various aluminum concentrations and one ternary Fe-Al-Cr weld overlay were successfully deposited using a Gas Tungsten Arc Welding (GTAW) process and cracking susceptibility was evaluated on these coatings.
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
885600.pdf | 2518KB | download |