Aluminum Corrosion and Turbidity | |
Longtin, F.B. | |
Savannah River Site (S.C.) | |
关键词: Corrosion; Aluminium; Fuel Elements; Oxides; 22 General Studies Of Nuclear Reactors; | |
DOI : 10.2172/810370 RP-ID : DPSP-59-766 RP-ID : AT(07-2)-1 RP-ID : 810370 |
|
美国|英语 | |
来源: UNT Digital Library | |
【 摘 要 】
Aluminum corrosion and turbidity formation in reactors correlate with fuel sheath temperature. To further substantiate this correlation, discharged fuel elements from R-3, P-2 and K-2 cycles were examined for extent of corrosion and evidence of breaking off of the oxide film. This report discusses this study.