H1259 Container Foams: Performance Data on Aged Materials

Domeier, Linda

Sandia National Laboratories

关键词: Plastics;    Polyurethanes;    Density;    Age Dependence;    36 Materials Science;   

DOI  :  10.2172/796142
RP-ID  :  SAND2002-8113
RP-ID  :  AC04-94AL85000
RP-ID  :  796142

美国|英语

来源: UNT Digital Library

【 摘 要 】

Samples of the three cushioning foams used in the H1259 weapon storage container were obtained in 1997, 1998, 2000 and 2001 and tested for density, compression set and compressive strength using the same procedures specified for acceptance testing. Foams from six containers, all about 30 years old and located at Pantex, were evaluated. The bottom cushioning foam is a General Plastics polyurethane foam and the two side pads are rebonded polyurethane foams. All the tests were carried out at room temperature. When compared to the original acceptance requirements the foams were generally in-spec for density and compressive strength at 10% strain and were generally out-of-spec for compression set and compressive strength at 50% strain. Significant variability was noted in the performance of each foam sample and even more in the container-to-container foam performance. The container-to-container variability remains the major unknown in predicting the long-term suitability of these containers for continued use. The performance of the critical bottom cushion foams was generally more uniform and closer to the specified performance than that of the rebonded foams. It was judged that all the foams were adequate for continued use as storage container foams (not shipping) under controlled conditions to mitigate temperature extremes or high impact. This archived information is important in evaluations of the continued suitability for weapon storage use of the H1259 containers and other containers using the same foam cushions.