Fabrication of Efficient, Large Aperture Transmission Diffraction Gratings by Ion-Beam Etching

Nguyen, H T ; Bryan, S R ; Britten, J A ; Perry, M D

Lawrence Livermore National Laboratory

关键词: Amplification;    Compression;    Dielectric Materials;    Reflection;    Lasers;   

DOI  :  10.2172/15013515
RP-ID  :  UCRL-ID-140249-REV-1
RP-ID  :  W-7405-ENG-48
RP-ID  :  15013515

美国|英语

来源: UNT Digital Library

【 摘 要 】

The utilization of high-power short pulse laser employing chirped-pulse amplification (CPA) for material processing and inertial confinement research is widely increasing. The performance of these high-power CPA laser system continues to be limited by the ability of the pulse compression gratings to hold up to the high-average-power or high-peak-power of the laser. Pulse compression gratings used in transmission and fabricated out of bulk fused silica have intrinsically the highest laser damage threshold when compared with metal or multilayer dielectric gratings that work in reflection. LLNL has developed processing capability to produce high efficiency fused silica transmission gratings at sizes useful to future Petawatt-class systems, and has demonstrated high efficiency at smaller aperture. This report shows that fused silica diffraction exhibiting >95% efficiency into the -1 diffraction order in transmission (90{sup o} deflection of the incident light, at an incidence angle of 45{sup o} to the grating face). The microstructure of this grating consisted of grooves ion-beam etched to a depth of 1.6 microns with a pitch of 0.75 microns, using a holographically produced photoresist mask that was subsequently stripped away in significance to the fabrication of the small scale high efficiency grating was the development of the processing technology and infrastructure for production of such gratings at up to 65 cm diameter. LLNL is the currently the only location in the world with the ability to coat, interferometrically expose, and ion etch diffractive optics at this aperture. Below, we describe the design, fabrication, performance and, the scaleup process for a producing a high-efficiency transmission grating on a 65 cm fused silica substrate.