RERTR-9 Summary Report

Perez, D. M.

Idaho National Laboratory

关键词: Hot Pressing;    Alloys;    Testing;    Irradiation;    Thermal Analysis Rertr-9 Irradiation Summary Report;   

DOI  :  10.2172/1023454
RP-ID  :  INL/EXT-10-18421
RP-ID  :  DE-AC07-05ID14517
RP-ID  :  1023454

美国|英语

来源: UNT Digital Library

【 摘 要 】

The RERTR-9 experiment was designed to test the effect of modified fuel/clad interfaces in monolithic fuel plates and to demonstrate that the addition of Si to the matrix material in dispersion plates continued to be effective at high loading (~8.5 g U/cc). Several monolithic fuel plates were fabricated by Hot Isostatic Pressing (HIP) and Friction Bonding (FB) with thin layers of Si inserted and by HIP with a Zr diffusion barrier between the fuel and cladding. Si was applied to the interface by thermal spray of Al Si mixtures and by the insertion of thin Si-rich Al alloy foil between the fuel/clad interface. The dispersion fuel plates were fabricated by semi-standard rolling techniques (the reduction by rolling was lowered to limit fabrication defects). Matrix materials consisted of Al-Si alloys and mixtures with various levels of Si. The following report summarizes the life of the RERTR-9A/B experiment through end of irradiation, including as-run neutronic analysis, thermal analysis and hydraulic testing results.