EVALUATION OF POTENTIAL ELUANTS FOR NON-ACID ELUTION OF CESIUM FROM RESORCINOL-FORMALDEHYDE RESIN

Adu-Wusu, K. ; Pennebaker, F.

Savannah River Site (S.C.)

关键词: Corrosion;    Acetates;    Carbon Steels;    Magnesium;    Waste Processing;   

DOI  :  10.2172/1003847
RP-ID  :  SRNL-STI-2010-00563R1
RP-ID  :  DE-AC09-08SR22470
RP-ID  :  1003847

美国|英语

来源: UNT Digital Library

【 摘 要 】

Small-column ion exchange (SCIX) units installed in high-level waste tanks to remove Cs-137 from highly alkaline salt solutions are among the waste treatment plans in the DOE-complex. Spherical Resorcinol-Formaldehyde (sRF) is the ion exchange resin selected for use in the Hanford Waste Treatment and Immobilization Plant (WTP). It is also the primary ion exchange material under consideration for SCIX at the Hanford site. The elution step of the multi-step ion exchange process is typically done with 0.5 M nitric acid. An acid eluant is a potential hazard in the event of a spill, leak, etc. because the high-level waste tanks are made of carbon steel. Corrosion and associated structural damage may ensue. A study has been conducted to explore non-acid elution as an alternative. Batch contact sorption equilibrium screening tests have been conducted with 36 potential non-acid eluants. The sorption tests involve equilibrating each cesium-containing eluant solution with the sRF resin for 48 hours at 25 C in a shaker oven. In the sorption tests, an eluant is deemed to have a high cesium elution potential if it minimizes cesium sorption onto the sRF resin. The top candidates (based on lowest cesium sorption distribution coefficients) include ammonium carbonate, ammonium carbonate/ammonium hydroxide, ammonium bicarbonate, rubidium carbonate, ammonium acetate, ammonium acetate/ammonium hydroxide, ammonium bicarbonate/ammonium hydroxide, calcium chloride, and magnesium chloride. A select few of the top candidate eluants from the screening tests were subjected to actual sorption (loading) and elution tests to confirm their elution ability. The actual sorption (loading) and elution tests mimicked the typical sRF-cesium ion exchange process (i.e., sorption or loading, caustic wash, water rinse, and elution) via batch contact sorption and quasi column caustic wash/water rinse/elution. The eluants tested included ammonium carbonate, ammonium acetate, calcium acetate, magnesium acetate, and nitric acid. Calcium acetate and magnesium acetate were substitutes for calcium chloride and magnesium chloride respectively due to corrosion concerns. Nitric acid was selected for benchmarking since it is the baseline cesium eluant for sRF resin. The cesium elution performance of ammonium carbonate and ammonium acetate was approximately the same as the benchmark eluant, nitric acid. Ninety-seven (97), 94, and 100% percent of the cesium sorbed or loaded were eluted by ammonium carbonate, ammonium acetate, and nitric acid was respectively. The performance of calcium acetate and magnesium acetate, on the other hand, was mediocre. Percent elution was 16 and 8 respectively.