PRELIMINARY STUDY OF CERAMICS FOR IMMOBILIZATION OF ADVANCED FUEL CYCLE REPROCESSING WASTES

Fox, K. ; Billings, A. ; Brinkman, K. ; Marra, J.

Savannah River Site (S.C.)

关键词: 36 Materials Science;    Fuel Cycle;    Wastes;    Scanning Electron Microscopy;    Zirconolite;   

DOI  :  10.2172/1001177
RP-ID  :  SRNL-STI-2010-00560
RP-ID  :  DE-AC09-08SR22470
RP-ID  :  1001177

美国|英语

来源: UNT Digital Library

【 摘 要 】

The Savannah River National Laboratory (SRNL) developed a series of ceramic waste forms for the immobilization of Cesium/Lanthanide (CS/LN) and Cesium/Lanthanide/Transition Metal (CS/LN/TM) waste streams anticipated to result from nuclear fuel reprocessing. Simple raw materials, including Al{sub 2}O{sub 3}, CaO, and TiO{sub 2} were combined with simulated waste components to produce multiphase ceramics containing hollandite-type phases, perovskites (particularly BaTiO{sub 3}), pyrochlores, zirconolite, and other minor metal titanate phases. Identification of excess Al{sub 2}O{sub 3} via X-ray Diffraction (XRD) and Scanning Electron Microscopy with Energy Dispersive Spectroscopy (SEM/EDS) in the first series of compositions led to a Phase II study, with significantly reduced Al{sub 2}O{sub 3} concentrations and increased waste loadings. Three fabrication methodologies were used, including melting and crystallizing, pressing and sintering, and Spark Plasma Sintering (SPS), with the intent of studying phase evolution under various sintering conditions. XRD and SEM/EDS results showed that the partitioning of the waste elements in the sintered materials was very similar, despite varying stoichiometry of the phases formed. The Phase II compositions generally contained a reduced amount of unreacted Al{sub 2}O{sub 3} as identified by XRD, and had phase assemblages that were closer to the initial targets. Chemical composition measurements showed no significant issues with meeting the target compositions. However, volatilization of Cs and Mo was identified, particularly during melting, since sintering of the pressed pellets and SPS were performed at lower temperatures. Partitioning of some of the waste components was difficult to determine via XRD. SEM/EDS mapping showed that those elements, which were generally present in small concentrations, were well distributed throughout the waste forms. Initial studies of radiation damage tolerance using ion beam irradiation at Los Alamos National Laboratory (LANL) showed little if any modification of the material after irradiation. Additional study in this area is needed. Chemical durability was briefly studied using the Product Consistency Test (PCT). Most of the elements measured were retained by the ceramic waste forms, indicating good chemical durability. Cs, Mo, and Rb were released at somewhat higher rates as compared to the matrix components, although benchmark compositions and additional characterization are needed in order to qualify the PCT results.