3D Printed Glass: Surface Finish and Bulk Properties as a Function of the Printing Process-->
It is impossible to print glass directly from a melt, layer by layer. Glass is not only very sensitive to temperature gradients between different layers but also to the cooling process. To achieve a glass state the melt, has to be cooled rapidly to avoid crystallization of the material and then annealed to remove cooling induced stress. In 3D-printing of glass the objects are shaped at room temperature and then fired. The material properties of the final objects are crucially dependent on the frit size of the glass powder used during shaping, the chemical formula of the binder and the firing procedure. For frit sizes below 250 *m, we seem to find a constant volume of pores of less than 5%. Decreasing frit size leads to an increase in the number of pores which then leads to an increase of opacity. The two different binders, 2- hydroxyethyl cellulose and carboxymethylcellulose sodium salt, generate very different porosities. The porosity of samples with 2-hydroxyethyl cellulose is similar to frit-only samples, whereas carboxymethylcellulose sodium salt creates a glass foam. The surface finish is determined by the material the glass comes into contact with during firing.
【 预 览 】
Copyright © 2016 中国科学院文献情报中心
京公网安备340104078870146号  OAinOne平台基于对开放资源的发现、遴选和评价方式，发现、获取、集成9类优质的开放科技资源，包括开放期刊、开放会议论文、开放课件、科技政策、开放学位论文、开放图书、开放科技报告、科研项目、开放科学数据。同时，为实现开放知识资源普遍服务、个性化服务、精准服务，基于OAinONE集成的丰富开放资源，开发建设领域开放知识资源服务定制工具(OAtoYOU)、开放资源评价评估体系（OAEvaluation），建设集成OAinONE资源及其他第三方资源的OA Hub，及其面向我院分布式大数据知识资源系统及其他第三方的开放接口服务，并打造特色专题数据库产品建设，包括科技政策集成及趋势平台、开放课程大讲堂等。此外，OAinOne构建开放知识资源建设的可持续发展机制，支持我院研究所特色馆藏资源、自建资源、古籍资源等在OAinONE平台上的集成、开放、共享。
| |||||||||
download
878987797
028-85220240