Apple Strength Issues

Syn, C

关键词: ALUMINIUM;    APPLES;    CHEMICAL COMPOSITION;    DISTRIBUTION;    ELONGATION;    FIGS;    HEATING;    HEATING SYSTEMS;    INDUCTION;    MANUFACTURING;    PROCESSING;    TENSILE PROPERTIES;    YIELD STRENGTH;   

DOI  :  10.2172/972126
RP-ID  :  LLNL-TR-422311
PID  :  OSTI ID: 972126
Others  :  TRN: US201006%%894

学科分类：材料科学（综合）

美国|英语

来源: SciTech Connect

【 摘 要 】

Strength of the apple parts has been noticed to decrease, especially those installed by the new induction heating system since the LEP campaign started. Fig. 1 shows the ultimate tensile strength (UTS), yield strength (YS), and elongation of the installed or installation-simulated apples on various systems. One can clearly see the mean values of UTS and YS of the post-LEP parts decreased by about 8 ksi and 6 ksi respectively from those of the pre-LEP parts. The slight increase in elongation seen in Fig.1 can be understood from the weak inverse relationship between the strength and elongation in metals. Fig.2 shows the weak correlation between the YS and elongation of the parts listed in Fig. 1. Strength data listed in Figure 1 were re-plotted as histograms in Figs. 3 and 4. Figs. 3a and 4a show histograms of all UTS and YS data. Figs. 3b and 4b shows histograms of pre-LEP data and Figs. 3c and 4c of post-LEP data. Data on statistical scatter of tensile strengths have been rarely published by material suppliers. Instead, only the minimum 'guaranteed' strength data are typically presented. An example of strength distribution of aluminum 7075-T6 sheet material, listed in Fig. 5, show that its scatter width of both UTS and YS for a single sheet can be about 6 ksi and for multi-lot scatter can be as large as 11 ksi even though the sheets have been produced through well-controlled manufacturing process. By approximating the histograms shown in Figs. 3 and 4 by a Gaussian or similar type of distribution curves, one can plausibly see the strength reductions in the later or more recent apples. The pre-LEP data in Figs. 3b and 4b show wider scatter than the post-LEP data in Figs. 3c and 4c and seem to follow the binomial distribution of strength indicating that the apples might have been made from two different lots of material, either from two different vendors or from two different melts of perhaps slightly different chemical composition by a single vendor. The post-LEP apples seem to have been from a single batch of material. The pre-LEP apples of the weak strength and the post-LEP apples with even weaker strength could have been made of the same batch of material, and the small strength differential might be due to the difference in the induction heating system. If the pre-LEP apples with the lower strength and the post LEP apples are made from the same batch of material, their combined scatter of strength data would be wider and can be understood as a result of the additional processing steps of stress relief and induction heating as discussed.