Evaluation of Alumina-Forming Austenitic Stainless Steel Alloys in Microturbines

Brady, M.P. ; Matthews, W.J. (Capstone Turbine Corp.)

关键词: AIR;    ALLOYS;    CONSTRUCTION;    ELECTRON PROBES;    ENERGY EFFICIENCY;    ENGINES;    EVALUATION;    MICROANALYSIS;    MICROSCOPY;    ORNL;    OXIDATION;    STAINLESS STEELS;    TESTING;    TURBINES;   

DOI  :  10.2172/988341
RP-ID  :  NFE-08-01392
PID  :  OSTI ID: 988341
Others  :  TRN: US201018%%640

学科分类：材料科学（综合）

美国|英语

来源: SciTech Connect

【 摘 要 】

Oak Ridge National Laboratory (ORNL) and Capstone Turbine Corporation (CTC) participated in an in-kind cost share cooperative research and development agreement (CRADA) effort under the auspices of the Energy Efficiency and Renewable Energy (EERE) Technology Maturation Program to explore the feasibility for use of developmental ORNL alumina-forming austenitic (AFA) stainless steels as a material of construction for microturbine recuperator components. ORNL delivered test coupons of three different AFA compositions to CTC. The coupons were exposed in steady-state elevated turbine exit temperature (TET) engine testing, with coupons removed for analysis after accumulating ~1,500, 3,000, 4,500, and 6,000 hours of operation. Companion test coupons were also exposed in oxidation testing at ORNL at 700-800?��C in air with 10% H2O. Post test assessment of the coupons was performed at ORNL by light microscopy and electron probe microanalysis. The higher Al and Nb containing AFA alloys exhibited excellent resistance to oxidation/corrosion, and thus show good promise for recuperator applications.