RERTR-9 Summary Report | |
D. M. Perez | |
关键词: ALLOYS; BONDING; DEFECTS; DIFFUSION BARRIERS; FABRICATION; FRICTION; FUEL PLATES; HOT PRESSING; HYDRAULICS; IRRADIATION; MATRIX MATERIALS; MIXTURES; PLATES; ROLLING; TESTING; THERMAL ANALYSIS RERTR-9 Irradiation Summary Report; | |
DOI : 10.2172/1023454 RP-ID : INL/EXT-10-18421 PID : OSTI ID: 1023454 Others : TRN: US1104680 |
|
学科分类:核能源与工程 | |
美国|英语 | |
来源: SciTech Connect | |
【 摘 要 】
The RERTR-9 experiment was designed to test the effect of modified fuel/clad interfaces in monolithic fuel plates and to demonstrate that the addition of Si to the matrix material in dispersion plates continued to be effective at high loading (~8.5 g U/cc). Several monolithic fuel plates were fabricated by Hot Isostatic Pressing (HIP) and Friction Bonding (FB) with thin layers of Si inserted and by HIP with a Zr diffusion barrier between the fuel and cladding. Si was applied to the interface by thermal spray of Al Si mixtures and by the insertion of thin Si-rich Al alloy foil between the fuel/clad interface. The dispersion fuel plates were fabricated by semi-standard rolling techniques (the reduction by rolling was lowered to limit fabrication defects). Matrix materials consisted of Al-Si alloys and mixtures with various levels of Si. The following report summarizes the life of the RERTR-9A/B experiment through end of irradiation, including as-run neutronic analysis, thermal analysis and hydraulic testing results.
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO201704210002419LZ | 20028KB | download |