ANALYTICAL RESULTS OF MOX COLEMANITE CONCRETE SAMPLE POURED MAY 4, 2012
Cozzi, A. ; Best, D. ; Reigel, M.
关键词: BEARINGS;    BORON;    CONCRETES;    CRITICALITY;    DESIGN;    DISSOLUTION;    FABRICATION;    HYDROGEN;    MIXED OXIDE FUELS;    NEUTRON ABSORBERS;    NEUTRON FLUX;    PEROXIDES;    SAVANNAH RIVER;    SODIUM;   
DOI  :  10.2172/1043261
RP-ID  :  SRNL-STI-20120-00344
PID  :  OSTI ID: 1043261
Others  :  TRN: US1203268
美国|英语
来源: SciTech Connect
PDF
【 摘 要 】

The Mixed Oxide Fuel Fabrication Facility (MFFF) will use Colemanite bearing concrete neutron absorber panels credited with attenuating neutron flux in the criticality design analyses. The Savannah River National Laboratory is tasked with measuring the total density, partial hydrogen density, and partial boron density of the colemanite concrete. Sample 04 May 12/Test/S1-1, S1-2, and S1-3 was received on 5/9/2012 and analyzed. The total density measure by the ASTM method C 642 was 2.00 g/cm{sup 3}, within the lower bound of 1.88 g/cm{sup 3}. The partial hydrogen density of 6.35E-02 g/cm{sup 3} as measured using method ASTM E 1311 met the lower bound of 6.04E-02 g/cm{sup 3}. The measured partial boron density of 1.88E-01 g/cm{sup 3} exceeded the lower bound of 1.65E-01 g/cm{sup 3} when the sodium peroxide fusion dissolution method was used in place of the prescribed ASTM C 1301 method.

【 预 览 】
附件列表
Files Size Format View
RO201704190002773LZ 1063KB PDF download
  文献评价指标  
  下载次数:19次 浏览次数:24次