STATUS REPORT FOR AGING STUDIES OF EPDM O-RING MATERIAL FOR THE H1616 SHIPPING PACKAGE

Stefek, T. ; Daugherty, W. ; Skidmore, E.

关键词: AGING;    COMPRESSION;    CONTAINMENT;    DIENES;    ETHYLENE;    FORECASTING;    GASKETS;    HARDNESS;    HELIUM;    LEAK TESTING;    MAINTENANCE;    MECHANICAL PROPERTIES;    MONITORS;    MONOMERS;    PERFORMANCE;    PROPYLENE;    SAVANNAH RIVER PLANT;    SERVICE LIFE;    SPECIFICATIONS;    STRESS RELAXATION;    TENSILE PROPERTIES;    TESTING;    THICKNESS;   

DOI  :  10.2172/1050617
RP-ID  :  SRNL-STI-2012-00348
PID  :  OSTI ID: 1050617
Others  :  TRN: US201218%%1046

学科分类：社会科学、人文和艺术（综合）

美国|英语

来源: SciTech Connect

【 摘 要 】

This is an interim status report for tasks carried out per Task Technical Plan SRNL-STI-2011-00506. A series of tasks/experiments are being performed at the Savannah River National Laboratory to monitor the aging performance of ethylene propylene diene monomer (EPDM) Orings used in the H1616 shipping package. The data will support the technical basis to extend the annual maintenance of the EPDM O-rings in the H1616 shipping package and to predict the life of the seals at bounding service conditions. Current expectations are that the O-rings will maintain a seal at bounding normal temperatures in service (152 F) for at least 12 months. The baseline aging data review suggests that the EPDM O-rings are likely to retain significant mechanical properties and sealing force at bounding service temperatures to provide a service life of at least 2 years. At lower, more realistic temperatures, longer service life is likely. Parallel compression stress relaxation and vessel leak test efforts are in progress to further validate this assessment and quantify a more realistic service life prediction. The H1616 shipping package O-rings were evaluated for baseline property data as part of this test program. This was done to provide a basis for comparison of changes in material properties and performance parameters as a function of aging. This initial characterization was limited to physical and mechanical properties, namely hardness, thickness and tensile strength. These properties appear to be consistent with O-ring specifications. Three H1616-1 Containment Vessels were placed in test conditions and are aging at temperatures ranging from 160 to 300 F. The vessels were Helium leak-tested initially and have been tested at periodic intervals after cooling to room temperature to determine if they meet the criterion of leaktightness defined in ANSI standard N14.5-97 (< 1E-07 std cc air/sec at room temperature). To date, no leak test failures have occurred. The cumulative time at temperature ranges from 174 days for the 300 F vessel to 189 days for the 160 F vessel as of 8/1/2012. The compression stress-relaxation (CSR) behavior of H1616 shipping package O-rings is being evaluated to develop an aging model based on material properties. O-ring segments were initially aged at four temperatures (175 F, 235 F, 300 F and 350 F). These temperatures were selected to bound normal service temperatures and to challenge the seals within a reasonable aging period. Currently, samples aging at 300 F and 350 F have reached the mechanical failure point (end of life) which is defined in this study as 90% loss of initial sealing force. As a result, additional samples more recently began aging at {approx}270 F to provide additional data for the aging model. Aging and periodic leak testing of the full containment vessels, as well as CSR testing of O-ring segments is ongoing. Continued testing per the Task Technical Plan is recommended in order to validate the assumptions outlined in this status report and to quantify and validate the long-term performance of O-ring seals under actual service conditions.