Destructive Examination of Shipping Package 9975-02019

Daugherty, W. L.¹ 

[1]Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL)

关键词: MOISTURE;    INSPECTION;    PLUTONIUM;    CORROSION;    SAVANNAH RIVER PLANT;    THERMAL CONDUCTIVITY;    CONTAINERS;    CONTAINMENT;    FUNGI;    RESIDUES;    STAINS;    ABUNDANCE;    FLANGES;    ORIENTATION;    STORAGE K-Area;    surveillance;    9975 shipping package;   

DOI  :  10.2172/1262317
RP-ID  :  SRNL-STI--2016-00324
PID  :  OSTI ID: 1262317
Others  :  TRN: US1601597

学科分类：工程和技术（综合）

美国|英语

来源: SciTech Connect

【 摘 要 】

Destructive and non-destructive examinations have been performed on the components of shipping package 9975-02019 as part of a comprehensive SRS surveillance program for plutonium material stored in the K-Area Complex (KAC). During the field surveillance inspection of this package in KAC, two non-conforming conditions were noted: the axial gap of 1.577 inch exceeded the 1 inch maximum criterion, and two areas of dried glue residue were noted on the upper fiberboard subassembly. This package was subsequently transferred to SRNL for more detailed inspection and destructive examination. In addition to the conditions noted in KAC, the following conditions were noted: - Numerous small spots of corrosion were observed along the bottom edge of the drum. - In addition to the smeared glue residue on the upper fiberboard subassembly, there was also a small dark stain. - Mold was present on the side and bottom of the lower fiberboard subassembly. Dark stains from elevated moisture content were also present in these areas. - A dark spot with possible light corrosion was observed on the primary containment vessel flange, and corresponding rub marks were observed on the secondary containment vessel ID. - The fiberboard thermal conductivity in the radial orientation was above the specified range. When the test was repeated with slightly lower moisture content, the result was acceptable. The moisture content for both tests was within a range typical of other packages in storage. The observed conditions must be fully evaluated by KAC to ensure the safety function of the package is being maintained. Several factors can contribute to the concentration of moisture in the fiberboard, including higher than average initial moisture content, higher internal temperature (due to internal heat load and placement within the array of packages), and the creation of additional moisture as the fiberboard begins to degrade.