Hydrogen absorption properties of Li-Mg-N-H system

JOURNAL OF ALLOYS AND COMPOUNDS

卷:400

Article

Ichikawa, T ; Tokoyoda, K ; Leng, HY ; Fujii, H

关键词: hydrogen storage materials;    gas-solid reactions;    high-energy ball milling;    mechanochemical synthesis;    thermal analysis;   

DOI  :  10.1016/j.jallcom.2005.03.068

来源: Elsevier

【 摘 要 】

Isothermal hydrogen absorption properties of the ball milled mixture of 3Mg(NH2)(2) and 8LiH after dehydrogenation at 200 degrees C under high vacuum were investigated at two different temperatures of 150 and 200 degrees C. The pressure-composition isotherm (PCT) curve at 200 degrees C revealed a two-plateaus-like behavior, while the PCT curve at 150 degrees C showed a single-plateau-like behavior. The hydrogenated phases were composed of LiH and Mg(NH2)(2) under 9 MPa at 200 degrees C, while those were observed as mixed phases of LiH and LiNH2 at 150 degrees C without any trace of Mg(NH2)(2) in XRD measurements. These results indicate that there are two-step hydrogenation processes corresponding to high and low pressures at 200 degrees C, but the kinetics at 150 degrees C is too slow to proceed with the second hydrogenating step at high pressure region. (c) 2005 Elsevier B.V. All rights reserved.

【 授权许可】

Free