Microstructural and mechanical properties of oxide dispersion strengthened iron aluminides produced by mechanical milling and hot extrusion

JOURNAL OF ALLOYS AND COMPOUNDS

卷:834

Article

Durga, P., V^1,2  Prasad, K. Satya¹  Chandrasekhar, S. B.¹  Reddy, A., V¹  Bakshi, S. R.²  Vijay, R.¹ 

[1] Int Adv Res Ctr Powder Met & New Mat, Hyderabad 500005, India

[2] Indian Inst Technol Madras, Chennai 600036, Tamil Nadu, India

关键词: ODS;    Iron aluminides;    Mechanical milling;    Hot extrusion;    Tensile properties;   

DOI  :  10.1016/j.jallcom.2020.155218

来源: Elsevier

【 摘 要 】

Yttria dispersed Fe3Al alloy with a nominal composition of Fe-13Al-5Cr-0.18Ti-0.35 Y2O3 was produced by high energy ball milling followed by hot extrusion. The extruded and heat treated ODS Fe3Al exhibited both elongated and fine equi-axed grain structure in longitudinal direction, whereas, equi-axed grain structure was observed in transverse direction. Even though, both prealloyed as well as milled powder showed only FeAl phase, DO3 structured Fe3Al along with Y3Al5O12 and TiO phases existed in ODS Fe3Al. Presence of fine (7-25 nm corresponding to Y3Al5O12) and coarse (>25 nm, TiO) particles were observed in ODS Fe3Al. The material exhibited yield and ultimate tensile strengths of 1104 and 1308 MPa with 8% elongation. The improved strength and elongation are due to the presence of dispersoids and fine grained structure. (C) 2020 Elsevier B.V. All rights reserved.