Li conductivity in Li1+xTi2-xAlx(PO4)3 (0.3 ≤ x ≤ 0.7) ceramics prepared from sol-gel precursors

JOURNAL OF ALLOYS AND COMPOUNDS

卷:844

Article

Jimenez, R.¹  Sobrados, I.¹  Martinez, S.¹  Criado, M.²  Perea, B.³  Sanz, J.¹ 

[1] CSIC, Inst Ciencia Mat Madrid ICMM, Madrid 28049, Spain

[2] CSIC, Inst Ciencias Construcc Eduardo Torroja, C Serrano Galvache 4, Madrid 28033, Spain

[3] CSIC, Inst Opt Daza de Valdes, C Serrano 121, Madrid, Spain

关键词: Energy storage materials;    Sol-gel processes;    Ionic conduction;    Nuclear resonances;    Vacancy formation;   

DOI  :  10.1016/j.jallcom.2020.156051

来源: Elsevier

【 摘 要 】

Li1+xTi2-xAlx(PO4)(3) (LTAP)(x) = 0.3, 0.4, 0.5 and 0.7) compounds, prepared at 800 degrees C by sol-gel, have been studied by X-ray diffraction, Nuclear Magnetic Resonance, Scanning Electron Microscopy and Impedance Spectroscopy. The increment of lithium enhances Li-Li repulsions, favoring the creation of vacancies at the conduction paths intersection (M1 sites), increasing Li mobility along (... M1-M2-M1 ...) channels in NASICON phases. The partial elimination of segregated AlPO4, LiAlP2O7 and LiTiPO5 phases increased Ti, Al solubility in NASICON, improving overall conductivity in ceramics prepared at 950 degrees C. The maximum of bulk conductivity was produced in x = 0.4 sample, as a consequence of the creation of M1 vacancies and allocation of Li in M2 cavities with optimal Li/vacancy distribution. The presence of secondary phases increased grain boundary impedance, shifting maximum of overall conductivity to x = 0.3 compound. Obtained results are compared with those reported previously in LTPA samples prepared by the ceramic route. (C) 2020 Elsevier B.V. All rights reserved.