Modeling of ductile fracture: Significance of void coalescence

INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES

卷:43

Article

Gao, Xiaosheng ; Kim, Jinkook

关键词: ductile crack growth;    void coalescence;    critical strain;    failure surface;    stress triaxiality;    lode angle;    void shape;    failure mode;   

DOI  :  10.1016/j.ijsolstr.2005.08.008

来源: Elsevier

【 摘 要 】

In this paper void coalescence is regarded as the result of localization of plastic flow between enlarged voids. We obtain the failure criterion for a representative material volume (RMV) in terms of the macroscopic equivalent strain (E') as a function of the stress triaxiality parameter (T) and the Lode angle (theta) by conducting systematic finite element analyses of the void-containing RMV subjected to different macroscopic stress states. A series of parameter studies are conducted to examine the effects of the initial shape and volume fraction of theprimary void and nucleation, growth, and coalescence of secondary voids on the predicted failure surface E-c(T,theta). As an application, a numerical approach is proposed to predict ductile crack growth in thin panels of a 2024-T3 aluminum alloy, where a porous plasticity model is used to describe the void growth process and the expression for E-c. is calibrated using experimental data. The calibrated computational model is applied to predict crack extension in fracture specimens having various initial crack configurations and the numerical predictions agree very well with experimental measurements. (c) 2005 Elsevier Ltd. All rights reserved.

【 授权许可】

Free