High-rate lithium-sulfur batteries enabled by hierarchical porous carbons synthesized via ice templation

JOURNAL OF POWER SOURCES

卷:297

Article

Sahore, Ritu¹  Estevez, Luis P.¹  Ramanujapuram, Anirudh¹  DiSalvo, Francis J.²  Giannelis, Emmanuel P.¹ 

[1] Cornell Univ, Dept Mat Sci & Engn, Ithaca, NY 14853 USA

[2] Cornell Univ, Dept Chem & Chem Biol, Ithaca, NY 14853 USA

关键词: Hierarchical porous carbons;    Lithium-sulfur batteries;    Cyclic performance;    Porosity dependence;    Lithium nitrate;   

DOI  :  10.1016/j.jpowsour.2015.07.068

来源: Elsevier

【 摘 要 】

We report the performance of a series of hierarchical porous carbons (HPCs) with extremely high surface areas of up to 2340 m(2) g(-1) with total pore volume of up to 3.8 cm(3) g(-1) as supports for sulfur for Li-S batteries. The hierarchical structure of the carbon originating from interconnected large mesopores (10-50 nm), small mesopores (2-10 nm) and micropores (<2 nm) makes the total available surface area highly accessible, resulting in excellent electrode kinetics. At high C-rates of 2 C and 5 C, large specific capacities of 647 mA h g(-1) and 503 mA h g(-1), respectively, were obtained after 200 cycles. In addition, we also systematically show that the cyclic stability is independent of the size of the pores sulfur is initially confined in, when LiNO3 is used as the electrolyte additive, indicating that capacity fade due to polysulfide shuttle is effectively eliminated and that it is not related to pore size anymore. (C) 2015 Elsevier B.V. All rights reserved.