Dense integration of solvent-free electrodes for Li-ion supercabattery with boosted low temperature performance

JOURNAL OF POWER SOURCES

卷:473

Article

Zhou, Haitao¹  Liu, Menghao¹  Gao, Hongquan¹  Hou, Dong¹  Yu, Chongchen¹  Liu, Chao¹  Zhang, Dong¹  Wu, Jian-chun¹  Yang, Jianhong¹  Chen, De² 

[1] Jiangsu Univ, Sch Mat Sci & Engn, Zhenjiang 212013, Jiangsu, Peoples R China

[2] Norwegian Univ Sci & Technol, Dept Chem Engn, N-7491 Trondheim, Norway

关键词: Solvent-free electrodes;    Low-temperature;    Free-standing films;    PTFE fibration;    Eutectic electrolytes;    Hot-rolling;   

DOI  :  10.1016/j.jpowsour.2020.228553

来源: Elsevier

【 摘 要 】

Supercabatteries combine the advantages of high power and energy density performances. However, the electrodes are always fabricated using high surface area materials and traditional slurry coating method containing the solvent mixing and drying processes, which are less controlled, energy-intensive, and environmentally unfriendly. Herein, we report a solvent-free method in pilot stage, combining a high-speed air blowing, hot-rolling, and hot overlying process. The carbon materials with high content of 40% are mixed in the LiFePO4-activated carbons cathode and Li4Ti5O12-activated carbons anode, respectively. The compact densities of the thick solvent free electrodes (120 mu m, one-side) are almost-1.6 times of the values for the slurry coating electrodes. The solvent-free full cells show capacitive linear charge/discharge curves before the cell voltage plateaus. And these linear curves further mitigate the internal resistance drop at-40 degrees C using acetonitrile-assistant carbonate-based eutectic electrolytes. The full cell delivers high areal capacity of 1.4 mAh cm(-2) and volume energy density of 95 Wh L-1, which is almost 2 times higher than that of the slurry coating full cell. Moreover, the supercabattery with acetonitrile-assistant electrolyte shows excellent cycling retention of 92% for over 5000 cycles due to the self-passivated solid electrolyte interface formation and stable fibrous polytetrafluoroethylene net-like binding structure.