Evaluating the irradiation effects on the elastic properties of miniature monolithic SiC tubular specimens

JOURNAL OF NUCLEAR MATERIALS

卷:499

Article

Singh, G.¹  Koyanagi, T.¹  Petrie, C.¹  Terrani, K.¹  Katoh, Y.¹ 

[1] Oak Ridge Natl Lab, Oak Ridge, TN 37830 USA

关键词: Silicon carbide;    Accident tolerant fuel;    Cladding;    LWR;    Nondestructive testing;    SiC;    Nuclear;   

DOI  :  10.1016/j.jnucmat.2017.10.060

来源: Elsevier

【 摘 要 】

The initial results of a post-irradiation examination study conducted on CVD SiC tubular specimens irradiated under a high radial heat flux are presented herein. The elastic moduli were found to decrease more than that estimated based on previous studies. The significant decreases in modulus are attributed to the cracks present in the specimens. The stresses in the specimens, calculated through finite element analyses, were found to be greater than the expected strength of irradiated specimens, indicating that the irradiation-induced stresses caused these cracks. The optical microscopy images and predicted stress distributions indicate that the cracks initiated at the inner surface and propagated outward. (C) 2017 Elsevier B.V. All rights reserved.

【 授权许可】

Free