Production of more ideal uranium trioxide microspheres for the sol-gel microsphere pelletization process without the use of carbon

JOURNAL OF NUCLEAR MATERIALS

卷:515

Article

Hunt, R. D.¹  Collins, J. L.¹  Lloyd, M. H.¹  Finkeldei, S. C.¹ 

[1] Oak Ridge Natl Lab, POB 2008, Oak Ridge, TN 37831 USA

关键词: Uranium microspheres;    Internal gelation;    Pellets;   

DOI  :  10.1016/j.jnucmat.2018.12.029

来源: Elsevier

【 摘 要 】

Renewed interest by the U.S. Department of Energy in the sol-gel microsphere pelletization process led to an evaluation of dried uranium trioxide (UO3) microspheres produced without the use of carbon by the internal gelation process at Oak Ridge National Laboratory. An earlier study has shown that less dense UO3 microspheres led to uranium dioxide pellets with higher densities. This effort identified feed formulations that produced dried UO3 microspheres with the lowest tap densities for gelation temperatures of 333, 343, 353, and 363 K. The tap densities of these dried UO3 microspheres ranged from 680 to 820 kg/m(3), which were significantly lower than the previously reported low UO3 density of 900 kg/m(3). This study confirmed an earlier observation that the effects of gelation conditions on the properties of the gel sphere are complex since only two of the four best formulations were similar in composition. The need to age the wet gel spheres in the gelation medium for 20 min at the end of the experiment was also confirmed. (C) 2018 Elsevier B.V. All rights reserved.

【 授权许可】

Free