Close-up tracing of fatigue precrack evolution and reliable fracture toughness evaluation by the precracked specimens in an ITER specification W plate

JOURNAL OF NUCLEAR MATERIALS

卷:553

Article

Tokunaga, Kazutoshi¹  Matsuo, Satoru¹  Kurishita, Hiroaki²  Toyama, Takeshi³  Hasegawa, Makoto¹  Nakamura, Kazuo¹ 

[1] Kyushu Univ, Res Inst Appl Mech, Kasuga, Fukuoka 8168580, Japan

[2] High Energy Accelerator Res Org KEK, Inst Particle & Nucl Studies, Tokai, Ibaraki 3191106, Japan

[3] Tohoku Univ, Inst Mat Res, Oarai, Ibaraki 3111313, Japan

关键词: Tungsten;    Precracking;    Compression fatigue;    Tension fatigue;    Residual tensile stress;    Continuous in-situ tracing;    Grain boundary;    Fracture toughness;   

DOI  :  10.1016/j.jnucmat.2021.153054

来源: Elsevier

【 摘 要 】

Fracture toughness of the divertor armor in ITER needs to be elucidated for prediction of the response of armor materials to intense heat loading. The present study has been performed to establish a method for inserting a well, defined fatigue precrack into the test specimens and measure the reliable fracture toughness values of tungsten (W) materials that exhibit low temperature brittleness. Sub-sized, single edge notched bend (SENB) specimens with two orientations, L-T and T-L, taken from a commercially available pure W plate manufactured in accordance with the ITER material specifications (ITER specification W, ALMT-grade), were precracked in two-step fatigue loading: fully uniaxial compression fatigue to provoke a crack from the notch tip, and subsequent 3-point bend (3 PB) fatigue to extend the crack length for the minimization of influence of the residual tensile stresses generated by compression fatigue. During compression and 3 PB fatigue loading the fatigue crack was closely monitored by continuous insitu observations on the notch tip. Continuous tracing of the crack tip position has enabled capture of the fatigue cracking behavior as a kinematic response in a rolled W material, disclosing a marked difference in crack inducement and extension between the two orientations. 3 PB fracture testing of the precracked specimens at room temperature (RT) yielded similar to 10 MPa root m for the T-L and 12 similar to 13 MPa root m for the L-T orientation as fracture toughness: anisotropic variation in fracture toughness of the W plate is comparatively small. Fracture surface observations reveal that a crack path is entirely transgranular for the L-T, while crack propagation involves intergranular fracture to a large extent for the T-L orientation. These results obtained are discussed and compared with the literature data. (C) 2021 Elsevier B.V. All rights reserved.