Effect of the bainitic and martensitic microstructures on the hardening and embrittlement under neutron irradiation of a reactor pressure vessel steel

JOURNAL OF NUCLEAR MATERIALS

卷:465

Article

Marini, B.¹  Averty, X.²  Wident, P.¹  Forget, P.¹  Barcelo, F.¹ 

[1] Commissariat Energie Atom & Energies Alternat, DEN DANS DMN SRMA, F-91191 Gif Sur Yvette, France

[2] Commissariat Energie Atom & Energies Alternat, DEN DANS SEMT DM2S, F-91191 Gif Sur Yvette, France

关键词: RPV steel;    Irradiation induced embrittlement;    Microstructure;    Bainite;    Martensite;   

DOI  :  10.1016/j.jnucmat.2015.05.023

来源: Elsevier

【 摘 要 】

The hardening and the embrittlement under neutron irradiation of an A508 type RPV steel considering three different microstructures (bainite, bainite-martensite and martensite)have been investigated These microstructures were obtained by quenching after autenitization at 1100 degrees C. The irradiation induced hardening appears to depend on microstructure and is correlated to the yield stress before irradiation. The irradiation induced embrittlement shows a more complex dependence. Martensite bearing microstructures are more sensitive to non hardening embrittlement than pure bainite. This enhanced sensitivity is associated with the development of intergranular brittle facture after irradiation; the pure martensite being more affected than the bainite-martensite. It is of interest to note that this mixed microstructure appears to be more embrittled than the pure bainitic or martensitic phases in terms of temperature transition shift. This behaviour which could emerge from the synergy of the embrittlement mechanisms of the two phases needs further investigations. However, the role of microstructure on brittle intergranular fracture development appears to be qualitatively similar under neutron irradiation and thermal ageing. (C) 2015 Elsevier B.V. All rights reserved.