Film formation mechanism in glass lubrication by polymer latex dispersions

THIN SOLID FILMS

卷:518

Article

Beauvais, M.¹  Piezel, B.¹  Hamidi, F.¹  Villalobos, M.¹  Da Silva, C.²  Martin, E.²  Dalmas, D.¹  Barthel, E.¹ 

[1] CNRS St Gobain, UMR 125, Lab Surface Verre & Interfaces, F-93303 Aubervilliers, France

[2] St Gobain Res, F-93303 Aubervilliers, France

关键词: Glass;    Lubrication;    SnO2;    Roughness;    Surface chemistry;    Polymer;   

DOI  :  10.1016/j.tsf.2009.11.061

来源: Elsevier

【 摘 要 】

The stabilization of organic coatings by tin dioxide resulting in glass bottle lubrication was investigated on flat glass. The anchoring function of SnO2 Was assessed for a mixture of polyethylene and polymethylmethacrylate. Friction tests in air confirm the SnO2 anchoring property with the maintaining of the lubricant effect due to the polymer over large sliding distances. The persistence of the polymethylmethacrylate stretching band nu(C=O) on significant sliding distances in infrared microscopy experiments shows that the polymer coating stabilization results from the strong adhesion of the polymer on SnO2. The impact of roughness and surface chemistry on the stabilization of the polymer coating was tested. The suppression of the lubricant effect by surface chemistry alteration or by roughness modification of SnO2 suggests that roughness and Surface chemistry of SnO2 are both necessary for lubrication. (C) 2009 Elsevier B.V. All rights reserved.

【 授权许可】

Free