Electrochromic nickel oxide films and their compatibility with potassium hydroxide and lithium perchlorate in propylene carbonate: Optical, electrochemical and stress-related properties

THIN SOLID FILMS

卷:565

Article

Wen, Rui-Tao¹  Niklasson, Gunnar A.¹  Granqvist, Claes G.¹ 

[1] Uppsala Univ, Angstrom Lab, Dept Engn Sci, SE-75121 Uppsala, Sweden

关键词: Nickel oxide;    Thin film;    Electrochromism;    Stress;    Transmittance;    Durability;   

DOI  :  10.1016/j.tsf.2014.07.004

来源: Elsevier

【 摘 要 】

Porous nickel oxide films were deposited onto unheated indium tin oxide coated glass substrates by reactive dc magnetron sputtering. These films had a cubic NiO structure. Electrochromic properties were evaluated in 1 M potassium hydroxide (KOH) and in 1 M lithium perchlorate in propylene carbonate (Li-PC). Large optical modulation was obtained for similar to 500-nm-thick films both in KOH and in Li-PC (similar to 70% and similar to 50% at 550 nm, respectively). In KOH, tensile and compressive stresses, due to the expansion and contraction of the lattice, were found for films in their bleached and colored state, respectively. In Li-PC, compressive stress was seen both in colored and bleached films. Durability tests with voltage sweeps between -0.5 and 0.65 V vs Ag/AgCl in KOH showed good durability for 10,000 cycles, whereas voltage sweeps between 2.0 and 4.7 V vs Li/Li+ in Li-PC yielded significant degradation after 1000 cycles. (C) 2014 Elsevier B. V. All rights reserved.

【 授权许可】

Free