Tribocorrosion behavior of low friction TiSiCN nanocomposite coatings deposited on titanium alloy for biomedical applications

SURFACE & COATINGS TECHNOLOGY

卷:347

Article

Hatem, Andre¹  Lin, Jianliang²  Wei, Ronghua²  Torres, Ricardo D.¹  Laurindo, Carlos¹  de Souza, Gelson Biscaia³  Soares, Paulo¹ 

[1] Pontificia Univ Catolica Parana, Polytech Sch, Dept Mech Engn, BR-80215901 Curitiba, Parana, Brazil

[2] Southwest Res Inst, Dept Mat Engn, Surface Engn & Mat Chem, San Antonio, TX 78238 USA

[3] Univ Estadual Ponta Grossa, Phys Dept, BR-84030900 Ponta Grosso, PR, Brazil

关键词: Titanium alloy;    TiSiCN coatings;    Nanocomposites;    Adhesion;    Hardness;    Tribocorrosion;   

DOI  :  10.1016/j.surfcoat.2018.04.049

来源: Elsevier

【 摘 要 】

The quaternary Ti-Si-C-N nanocomposite is regarded to be promising one in the biomedical field due to its improved tribocorrosion performance and biocompatibility. The deposition of such material on biomedical components surfaces can extend its lifespan by minimizing wear debris and ion releasing inside the physiological environment. Therefore, this work investigates the tribocorrosion behavior of low friction Ti-Si-C-N nano-composite coatings applied on the ASTM F136 titanium alloy immersed in a phosphate-buffered solution (PBS). The coatings were obtained by the plasma-enhanced magnetron sputtering (PEMS) technique using an assorted precursor flow range of tetramethylsilane (TMS) and hexamethyldisilazane (HMDSN) liquid along with acetylene (C2H2) gas. Reciprocal sliding tribocorrosion tests were performed under PBS solution on the samples and compared to a Ti-6Al-4V bare alloy sample. The microstructure, morphology, chemical structure, mechanical properties, and adhesion of the coated samples were also evaluated. The results presented an expressive reduction of at least 97% in the wear rate of the low friction Ti-(Si)-C-N nanocomposite coatings compared to the titanium bare alloy sample. The tribocorrosion performance of the coated samples demonstrated a strong correlation within the Silicon and Carbon content presented on coatings chemical compositions. As consequence, the roles of nanocrystallites refinement, the presence of amorphous carbon region and the oxides generation were demonstrated as relevant characteristics to improve the tribocorrosion behavior of Ti-Si-C-N nano-composite.