Characterization of a laser-discrete quenched steel substrate/chromium system by dissolving coatings

SURFACE & COATINGS TECHNOLOGY

卷:201

Article

Li, Huaixue ; Zhang, Kun ; Chen, Guangnan ; Luo, Gengxing ; Ye Zhijun

关键词: interface;    electroplating;    chromium;    laser-discrete quenching;    dissolution edge effect;   

DOI  :  10.1016/j.surfcoat.2006.09.002

来源: Elsevier

【 摘 要 】

A laser-discrete quenched steel (LDQS) substrate/as-deposited chromium (top high-contraction (HC) and underlying low-contraction (LC) chromium) system was investigated by dissolving coatings in order to reveal the mechanism that the service life of the coated parts is largely improved using the hybrid technique of laser pre-quenching plus chromium post-depositing. It was found that the surface characteristics of the substrate, LC and HC chromium layer can be simultaneously revealed owing to the dissolution edge effect of chromium coatings. Moreover, the periodical gradient morphologies of the LDQS substrate are clearly shown: the surfaces of laser transformation-hardened regions are rather smooth; a lot of fine micro-holes exist in the transition zones; there are many micro-dimples in the original substrate. Furthermore, the novel method of dissolving coatings with sharp interfaces may be used to reveal the structural features of a substrate/coating system, explore the effect of the substrate on the initial microstructure and morphologies of coatings, and check the quality of the coated-parts. (c) 2006 Elsevier B.V. All rights reserved.

【 授权许可】

Free