Oxidation study of Pt-Al based coatings on γ-TiAl at 950 °C

SURFACE & COATINGS TECHNOLOGY

卷:287

Article

Ebach-Stahl, A.¹  Froehlich, M.² 

[1] DLR German Aerosp Ctr, Inst Mat Res, D-51170 Cologne, Germany

[2] Leibniz Inst Plasma Sci & Technol INP, Felix Hausdorff Str 2, D-17489 Greifswald, Germany

关键词: PtAl;    gamma-TiAl;    Oxidation;    Coating;    Magnetron sputtering;   

DOI  :  10.1016/j.surfcoat.2015.12.043

来源: Elsevier

【 摘 要 】

In the present study, Pt-based aluminide coatings were deposited on gamma-TiAl (Ti-45Al-8Nb-08C; at.%) by magnetron sputtering and tested under high temperature conditions. The Pt-content in the layer was varied (31, 47 and 100 at.%) to find an optimized oxidation resistant coating. The Pt-53Al coating showed the best oxidation resistance at 950 degrees C due to the formation of a continuous thin alumina layer on top compared to the fast oxidizing pure Pt and aluminum rich Pt-69Al coatings. Depending on the testing time different Pt-Ti-Al phases were formed below the grown oxide layer which is caused by the outward diffusion of Ti and the inward diffusion of Pt at the interface between coating and base material, respectively. Beside mass gain measurements microstructural examinations were performed via scanning electron microscopy (SEM), energy-dispersive X-Ray spectroscopy (EDS) as well as X-Ray diffractometry (XRD) to study the evolution of phase formation. (C) 2015 Elsevier B.V. All rights reserved.

【 授权许可】

Free