Anodizing of aluminium and AA 2024-T3 alloy in chromic acid: Effects of sulphate on film growth

SURFACE & COATINGS TECHNOLOGY

卷:309

Article

Elabar, D.¹  La Monica, G. R.²  Santamaria, M.²  Di Quarto, F.²  Skeldon, P.²  Thompson, G. E.² 

[1] Univ Manchester, Sch Mat, Corros & Protect Grp, Manchester M13 9PL, Lancs, England

[2] Univ Palermo, Fac Engn, Electrochem Mat Sci Lab, Viale Sci, I-90128 Palermo, Italy

关键词: Aluminium;    AA 2024 alloy;    Anodizing;    Chromic acid;    Sulphate;   

DOI  :  10.1016/j.surfcoat.2016.11.108

来源: Elsevier

【 摘 要 】

Chromic acid anodizing is important for the corrosion protection of aerospace aluminium alloys. Previous study has demonstrated that SO42- impurity in the chromic acid affects the film growth on aluminium at a voltage of 100 V. The present work further investigates aluminium and extends the study to industrial anodizing conditions (Bengough-Stuart (B-S) process) and to the AA 2024-T3 alloy. It is shown that SO42- concentrations between similar to 38-300 ppm reduce the film growth rate for aluminium anodized at 100V in comparison with an electrolyte than contains <= 1.5 ppm SO42-, whereas similar to 1500-3000 ppm SO42 have an opposite effect and lead to an unstable pore diameter. Under the B-S process, the film growth depends on the substrate composition, the SO42- content of the film, the film morphology and, for the alloy, oxygen generation. Corrosion tests of the alloy in 3.5% NaCl solution revealed better protection with films formed in chromic acid containing 38 ppm SO42- compared with <= 1.5 ppm SO42-, which are within the specified limits for sulphate impurity for chromic acid anodizing. The difference in corrosion protection is proposed to be related to the observed differences in the film morphologies; it is speculated that this may influence the retention of residues of chromate ions in the films. (C) 2016 Published by Elsevier B.V.