Low ice adhesion surfaces using microtextured hydrophobic tapes and their applications in refrigeration systems

SURFACE & COATINGS TECHNOLOGY

卷:351

Article

Mulroney, Alan T.¹  Kessler, Emily D.²  Combs, Steve³  Gupta, Mool C.¹ 

[1] Univ Virginia, Charles L Brown Dept Elect & Comp Engn, Charlottesville, VA 22904 USA

[2] Univ Virginia, Dept Chem, Charlottesville, VA 22904 USA

[3] Everidge LLC, Covesville, VA 22931 USA

关键词: Surface microtexture;    Teflon;    Anti-icing;    Hydrophobic;    Refrigeration systems;   

DOI  :  10.1016/j.surfcoat.2018.07.060

来源: Elsevier

【 摘 要 】

A low ice adhesion surface was generated using microtextured hydrophobic tapes. The surface microtexture was achieved by coating structural bonding tape with polytetrafluoroethylene (PTFE) powder. This technique required no chemicals or complex curing mechanisms. By introducing two powders with different average grain sizes, the surface microtexture was able to be varied for comparative testing. The average grain size ranges, and therefore the surface microtexture feature sizes, were 2 mu m to 4 mu m and 13 mu m to 21 mu m. The static contact angle varied between 102.1 degrees and 129.1 degrees, and the roll-off angle varied between 33.0 degrees and 14.6 degrees. A higher static contact angle and a lower roll-off angle were associated with a higher weight percent of the larger powder grains. The ice detachment pressure for the 1:10 powder mixture was 128 kPa, and the ice separation time under thermal defrost was 216 s. The powder coated structural bonding tape was applied to the cooling fan for a walk-in freezer. The behavior of ice accumulation due to humidity, as well as the ice removal due to defrost cycles, was qualitatively analyzed. It was found that the microtextured coating significantly reduced ice buildup on the fan and improved water collection during thermal defrost. The coating demonstrated the same level of performance after over 150 consecutive days of testing.