Crystal growth mechanism of calcium phosphate coatings on titanium by electrochemical deposition

SURFACE & COATINGS TECHNOLOGY

卷:334

Article

Mokabber, T.¹  Lu, L. Q.¹  van Rijn, P.²  Vakis, A. I.¹  Pei, Y. T.¹ 

[1] Univ Groningen, Fac Sci & Engn, Engn & Technol Inst Groningen, Dept Adv Prod Engn, Nijenborgh 4, NL-9747 AG Groningen, Netherlands

[2] Univ Groningen, Univ Med Ctr Groningen, Dept Biomed Engn, Ant Deusinglaan 1, NL-9713 AV Groningen, Netherlands

关键词: Calcium phosphate;    Coating;    Electrochemical deposition;    Nucleation and growth;    Morphology;   

DOI  :  10.1016/j.surfcoat.2017.12.011

来源: Elsevier

【 摘 要 】

The pulsed current electrochemical deposition of calcium phosphate (Ca-P) coatings on a titanium substrate was investigated in this study. The effects of applied voltage and H2O2 concentration in the electrolyte solution on the phase composition and coating morphology were studied using X-ray diffraction and scanning electron microscopy. At lower concentrations of H2O2, the coating consists of mixed phases of dicalcium phosphate dehydrate, octa-calcium phosphate, and hydroxyapatite, whereas increased H2O2 concentrations results in a dual phase of octa-calcium phosphate and hydroxyapatite being deposited. Furthermore, with increasing H2O2 concentration, the voltage must be reduced in order to avoid H-2 evolution. The best conditions for Ca-P deposition were achieved at -1.4 V and 1.5 wt% H2O2. The morphological changes at different deposition times as well as the crystallographic orientation of deposited crystals were studied using scanning electron microscopy and transmission electron microscopy. It was found that the crystal growth of Ca-P coatings is a time-dependent process. During the first stage of deposition (t = 1 min), the electrolyte is supersaturated and randomly oriented polycrystals of Ca-P nucleate and form nanoplates. During the second stage (t = 3 min), crystals grow slightly in a more oriented fashion and form micro-sized plates. During the third stage (t > 10 min), the deposited crystals grow in a highly directional manner and the morphology of the coating consists of elongated ribbon-like single crystals.