Optimization and thermal stability of TiAlN/Mo multilayers

SURFACE & COATINGS TECHNOLOGY

卷:200

Article; Proceedings Paper

Tavares, CJ ; Vidrago, C ; Rebouta, L ; Rivière, JP ; Le Bourhis, E ; Denanot, MF

关键词: multilayers;    thermal stability;    hardness;    stress;    roughness;    interdiffusion;   

DOI  :  10.1016/j.surfcoat.2005.02.099

来源: Elsevier

【 摘 要 】

In this work we focus on the optimization and thermal stability of nanocomposite TiAlN/Mo multilayers that were produced by reactive magnetron sputtering on high-speed steel substrates, with modulation periods below 5 nm. These multilayers were annealed between 600 - 900 degrees C for 1 h in a vacuum furnace. Preliminary X-ray results reveal that these coatings are very stable up to 900 degrees C, since the multilayer chemical modulation is not severely affected. At intermediate annealing temperatures the modulation period decreases due to interdiffusion at the interface, resulting in a thicker interface between metal/nitride and hence decreasing the thickness of those layers. (c) 2005 Elsevier B.V. All rights reserved.

【 授权许可】

Free