Acoustic emission analysis on tensile failure of air plasma-sprayed thermal barrier coatings

SURFACE & COATINGS TECHNOLOGY

卷:206

Article

Yao, W. B.^1,2  Dai, C. Y.^1,2  Mao, W. G.^1,2,3  Lu, C.⁴  Yang, L.^1,2  Zhou, Y. C.^1,2 

[1] Xiangtan Univ, Fac Mat Optoelect & Phys, Xiangtan 411105, Hunan, Peoples R China

[2] Xiangtan Univ, Key Lab Low Dimens Mat & Applicat Technol, Minist Educ, Xiangtan 411105, Hunan, Peoples R China

[3] Nanchang Hangkong Univ, Aeronaut Sci & Technol Key Lab Aeronaut Test & Ev, Nanchang 330063, Jiangxi, Peoples R China

[4] Curtin Univ, Dept Mech Engn, Perth, WA 6845, Australia

关键词: Thermal barrier coating;    Acoustic emission;    Fast Fourier transform;    Fracture mode;   

DOI  :  10.1016/j.surfcoat.2012.03.050

来源: Elsevier

【 摘 要 】

An acoustic emission technique was used to monitor the cracking behavior and fracture process of thermal barrier coatings subjected to tensile loading. Acoustic emission signals were extracted and preformed by fast Fourier transform, and their characteristic frequency spectrums and dominant bands were obtained to reveal fracture modes. Three different characteristic frequency bands were confirmed, corresponding to substrate deformation, surface vertical cracking and interface delamination, with the aid of scanning electronic microscopy observations. A map of the tensile failure mechanism of air plasma-sprayed thermal barrier coatings was established. The fracture strength and interfacial shear strength were estimated as 45.73 +/- 3.92 MPa and 20.51 +/- 1.74 MPa, respectively, which are well in agreement with available results. (C) 2012 Elsevier B.V. All rights reserved.