Austempered Compacted Graphite Iron - Influence of austempering temperature and time on microstructural and mechanical properties
Article
Ghasemi, Rohollah1  Hassan, Inamul1  Ghorbani, Arvin2  Dioszegi, Attila1 
[1] Jonkoping Univ, Sch Engn, Dept Mat & Mfg, POB 1026, SE-55111 Jonkoping, Sweden
[2] Bodycote Gothenburg, Spadegatan 23,POB 124, SE-42423 Gothenburg, Sweden
关键词: Austenitising;    Austempered CGI;    Ausferrite matrix;    Retained austenite;    Mechanical properties;    EBSD;   
DOI  :  10.1016/j.msea.2019.138434
来源: Elsevier
PDF
【 摘 要 】

This study investigates the effect of austempering temperature and time on the microstructural and mechanical properties of unalloyed Compacted Graphite Iron (CGI) with an initially ferritic matrix structure. The as-cast CGI samples were first austenitised at 900 degrees C for 60 min in a furnace, then austempered in a closed salt bath at three austempering temperatures - 275, 325, and 375 degrees C - for different times; 30, 60, 90, and 120 min. Tensile properties, Brinell, Vickers and Rockwell C hardness values were evaluated for the as-cast and austempered CGI ones. LOM and SEM, EBSD analysis techniques were used for microstructure and phase analysis. A mixture of acicular ferrite and retained austenite was achieved in the austempered CGI samples. In general, a decrease in austempering temperature resulted in a decrease in retained austenite content, corresponding improvements in hardness and tensile strength, and a decrease in elongation values.