Effect of volume fraction and particle size on the microstructure and plastic deformation of Mg-Y2O3 composites

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

卷:419

Article

Garcés, G ; Rodríguez, M ; Pérez, P ; Adeva, P

关键词: magnesium;    metal matrix composites (MMC);    plastic deformation;   

DOI  :  10.1016/j.msea.2006.01.026

来源: Elsevier

【 摘 要 】

The plastic behaviour at room temperature of magnesium and magnesium metal matrix composites reinforced with yttria particles of two sizes is studied. All the materials are produced by powder metallurgy. During extrusion both the unreinforced magnesium and the composites develop a fibre texture with the {1 0 (1) over bar 0} planes perpendicular to the extrusion direction. The fibre intensity decreases as the volume fraction of yttria particles increases. A tension/cornpression asymmetry is observed. The extrusion texture prevents deformation by the basal slip system in both tension and compression. Deformation in the {1 0 (1) over tilde 2} {1 0 (1) over tilde 1} twinning system is only possible in compression. As the volume fraction of yttria particles increases, the texture becomes more random and the tension/compression asymmetry tends to decrease and is eventually reversed. The composites reinforced with the smallest ceramic particles present the highest yield stress. (c) 2006 Elsevier B.V. All rights reserved.

【 授权许可】

Free