A new method for grain refinement in magnesium alloy: High speed extrusion machining

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

卷:651

Article

Liu, Yao¹  Cai, Songlin²  Dai, Lanhong³ 

[1] Univ Sci & Technol Beijing, Sch Math & Phys, Beijing 100083, Peoples R China

[2] State Grid Corp China, China Elect Power Res Inst, Beijing 100192, Peoples R China

[3] Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China

关键词: High speed extrusion machining;    Magnesium alloy;    Grain refinement;    Dynamic recrystallization;   

DOI  :  10.1016/j.msea.2015.11.046

来源: Elsevier

【 摘 要 】

Magnesium alloys have received broad attentions in industry due to their competitive strength to density ratio, but the poor ductility and strength limit their wide range of applications as engineering materials. A novel severe plastic deformation (SPD) technique of high speed extrusion machining (HSEM) was used here. This method could improve the aforementioned disadvantages of magnesium alloys by one single processing step. In this work, systematic HSEM experiments with different chip thickness ratios were conducted for magnesium alloy AZ31B. The microstructure of the chips reveals that HSEM is an effective SPD method for attaining magnesium alloys with different grain sizes and textures. The magnesium alloy with bimodal grain size distribution has increased mechanical properties than initial sample. The electron backscatter diffraction (EBSD) analysis shows that the dynamic recrystallization (DRX) affects the grain refinement and resulting hardness in AZ31B. Based on the experimental observations, a new theoretical model is put forward to describe the effect of DRX on materials during HSEM. Compared with the experimental measurements, the theoretical model is effective to predict the mechanical property of materials after HSEM. (c) 2015 Elsevier B.V. All rights reserved.