Interaction between Fe66Cr10Nb5B19 metallic glass and aluminum during spark plasma sintering

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

卷:799

Article

Dudina, Dina V.^1,2,3  Bokhonov, Boris B.³  Batraev, Igor S.¹  Amirastanov, Yusif N.²  Ukhina, Arina V.³  Kuchumova, Ivanna D.^1,2  Legan, Mikhail A.^1,2  Novoselov, Aleksey N.¹  Gerasimov, Konstantin B.³  Bataev, Ivan A.²  Georgarakis, Konstantinos⁴  Koga, Guilherme Yuuki⁵  Guo, Yaofeng⁵  Botta, Walter Jose⁵  Jorge, Alberto Moreira, Jr.^5,6,7 

[1] RAS, SB, Lavrentyev Inst Hydrodynam, Lavrentyev Ave 15, Novosibirsk 630090, Russia

[2] Novosibirsk State Tech Univ, K Marx Ave 20, Novosibirsk 630073, Russia

[3] RAS, SB, Inst Solid State Chem & Mechanochem, Kutateladze Str 18, Novosibirsk 630128, Russia

[4] Cranfield Univ, Sch Aerosp Transport & Mfg, Cranfield MK43 0AL, Beds, England

[5] Univ Fed Sao Carlos, Dept Mat Sci & Engn, Via Washington Luiz,Km 235, BR-13565905 Sao Carlos, SP, Brazil

[6] Grenoble Alpes Univ, CNRS, LEPMI, F-38000 Grenoble, France

[7] SIMAP, F-38000 Grenoble, France

关键词: Metal matrix composites;    Sintering;    Microstructure;    Scanning electron microscopy;    Hardness;   

DOI  :  10.1016/j.msea.2020.140165

来源: Elsevier

【 摘 要 】

In the area of metal matrix composites, novel reinforcing options are currently being evaluated. Particles of amorphous alloys present an interesting possibility to reinforce soft metals. In the present work, the interaction between Fe66Cr10Nb5B19 metallic glass and aluminum during spark plasma sintering (SPS) was studied for the first time. In order to trace the phase and microstructural changes upon sintering, mixtures containing 20 vol% and 50 vol% of metallic glass were subjected to SPS at 500-570 degrees C. After SPS at 500 degrees C, no reaction layer be-tween the metallic glass particles and aluminum was observed. After SPS at 570 degrees C, a reaction layer containing Fe2Al5 and FeAl3 formed around the Fe-based cores. The Vickers hardness of composites obtained from mixtures containing 20 vol% Fe66Cr10Nb5B19 at 540 degrees C was 75 HV and increased to 280 HV after sintering at 570 degrees C due to the formation of thicker reaction layers at the interface. The hardness of the composite sintered from the mixture containing 20 vol% Fe66Cr10Nb5B19 at 570 degrees C was between the values predicted by Reuss and Voigt models. Comparison of results of SPS of the powder mixtures with those of SPS of a pre-compacted pellet and electric current-free annealing suggests that local heating at the interface caused by interfacial resistance may be an important factor influencing the reaction advancement at the interface and the formation of Al-containing intermetallics.