Micromechanical and microstructure analysis of strain-induced phenomena in ultrasonic additively-manufactured Al-6061 alloy
Article
Cakmak, Ercan1  Gussev, Maxim N.2  Sridharan, Niyanth1  Seren, M. Hazar1,3  An, Ke4  Wang, Hsin1  Terrani, Kurt A.2 
[1] Oak Ridge Natl Lab, Mat Sci & Technol Div, Oak Ridge, TN 37831 USA
[2] Oak Ridge Natl Lab, Reactor & Nucl Syst Div, Oak Ridge, TN 37831 USA
[3] Columbia Univ, Dept Appl Phys & Appl Math, New York, NY 10027 USA
[4] Oak Ridge Natl Lab, Neutron Scattering Div, Oak Ridge, TN 37831 USA
关键词: Aluminum alloys;    X-ray analysis;    Electron microscopy;    Micromechanits;    Stress/strain measurements;    Plasticity;   
DOI  :  10.1016/j.msea.2019.138533
来源: Elsevier
PDF
【 摘 要 】

This work investigates the anisotropic mechanical behavior (both macro and micro) of A16061 alloy samples manufactured using ultrasonic additive manufacturing. Samples from both sonotrode travel and vibration directions (TD and VD, respectively) were investigated in the as-built and aged (8 hat 180 degrees C under Argon gas) conditions. The aged VD-specimens showed appearance and propagation of Luders-like band, which did not exist in the TD-specimens, deformed at the same strain rate. X-ray diffraction, x-ray computed tomography, scanning electron microscopy, laser flash technique and in-situ loading with neutron diffraction were used to characterize the material and its hardening behavior during straining. Aging was mainly found to lead to relaxation of stresses, induced by the build process, some decrease in yield stress, and potential secondary phase reprecipitation. Stress partitioning, revealed via in situ neutron diffraction, showed that one of grain families, (110) parallel to tensile axis, revealed strain softening at small strain range. This texture component, (110) parallel to tensile axis, dominated the structure of VD-specimens, and was one of key factors stimulating band appearance and propagation.

【 授权许可】