Mineralization of organic pollutants by anodic oxidation using reactive electrochemical membrane synthesized from carbothermal reduction of TiO2

WATER RESEARCH

卷:131

Article

Trellu, Clement¹  Coetsier, Clemence¹  Rouch, Jean-Christophe¹  Esmilaire, Roseline²  Rivallin, Matthieu²  Cretin, Marc²  Causserand, Christel¹ 

[1] Univ Toulouse, CNRS, INPT, Lab Genie Chim,UPS, Toulouse, France

[2] CNRS, ENSCM, UM, Inst European Membranes,UMR 5635, Montpellier, France

关键词: Anodic oxidation;    Electro-oxidation;    Reactive electrochemical membrane;    Organic pollutants;    Sub-stoichiometric titanium oxide;    Mineralization;   

DOI  :  10.1016/j.watres.2017.12.070

来源: Elsevier

【 摘 要 】

Reactive Electrochemical Membrane (REM) prepared from carbothermal reduction of TiO2 is used for the mineralization of biorefractory pollutants during filtration operation. The mixture of Ti4O7 and Ti5O9 Magneli phases ensures the high reactivity of the membrane for organic compound oxidation through (OH)-O-center dot mediated oxidation and direct electron transfer. In cross-flow filtration mode, convection-enhanced mass transport of pollutants can be achieved from the high membrane permeability (3300 LMH bar(-1)). Mineralization efficiency of oxalic acid, paracetamol and phenol was assessed as regards to current density, transmembrane pressure and feed concentration. Unprecedented high removal rates of total organic carbon and mineralization current efficiency were achieved after a single passage through the REM, e.g. 47 g m(-2) h(-1) - 72% and 6.7 g m(-2) h(-1) - 47% for oxalic acid and paracetamol, respectively, at 15 mA cm(-2). However, two mechanisms have to be considered for optimization of the process. When the TOC flux is too high with respect to the current density, aromatic compounds polymerize in the REM layer where only direct electron transfer occurs. This phenomenon decreases the oxidation efficiency and/or increases REM fouling. Besides, O-2 bubbles sweeping at high permeate flux promotes O-2 gas generation, with adverse effect on oxidation efficiency. (C) 2017 Elsevier Ltd. All rights reserved.