Does repeated autoclave sterilization cause changes in the color and fragility of fiberglass reinforced resin crowns?

BMC Oral Health

Research

Seçil Çaliskan¹  Ebru Delikan²  Canan Özdemir³  Ahmet Çalışkan⁴ 

[1] Department of Pediatric Dentistry, Faculty of Dentistry, Eskişehir Osmangazi University, Eskişehir, Turkey;Department of Pediatric Dentistry, Faculty of Dentistry, Nuh Naci Yazgan University, Kayseri, Turkey;Private Clinic, Eskişehir, Turkey;Special Uzman Diş Grup Oral and Dental Health Polyclinic, İzmit, Turkey;

关键词: Autoclave sterilization;    Color stability;    Failure analysis;    Fiberglass reinforced resin crowns;    Fracture resistance;   

DOI  :  10.1186/s12903-023-03254-x

 received in 2023-04-10, accepted in 2023-06-22,  发布年份 2023

来源: Springer

【 摘 要 】

BackgroundSince the effects of sterilization on the Fiberglass Reinforced Resin Crowns (FRRCs) is not well-known the aim of current study was to evaluate the effects of autoclave sterilization on the fracture resistance, color stability, and surface composition of FRRCs.MethodsA total of 48 crowns were used. The crowns were divided into three groups according to the sterilization number: no sterilization (Control Group), one sterilization (Group 1), and four sterilizations (Group 2). The microstructure of the three crowns from each group was evaluated using scanning electron microscopy (SEM) and energy-dispersive X-ray (EDX) spectroscopy. Thirteen FRRCs from each group were first used for color stability testing and then for the fracture resistance analysis. One-way analysis of variance (ANOVA), one-way repeated measures ANOVA, and paired t-tests were used in the statistical analysis.ResultsEDX results revealed that the weight% of surface silicon atoms in group 2 was significantly higher. Some crack lines could be observed on the SEM images. Statistically significant differences were found in color stability following the first and fourth sterilization cycles (p < .01). The increase in the sterilization cycle did not statistically decrease the fracture resistance of the FRRCs (p = .055); however, overall, a decreasing trend was observed in fracture resistance as the sterilization cycle increased.ConclusionsAutoclave sterilization caused some changes in the surface elemental composition and surface morphology of FRRCs. Avoiding unnecessary FRRC trials is important to reduce the number of sterilizations.