Investigation on BST-NZF Magnetoelectric Composites
article
Vishal Khatri1  Vinay Kumar2  Ashwani Kumar3  Shravan Kumar Meena4  Renu Rani5 
[1] Department of Physics, Nalanda College of Engineering;Department of Physics, COBS&H, CCS Haryana Agricultural University;Nanoscience laboratory Institute Instrumentation Centre;Department of Physics, Motilal Nehru College, University of Delhi, South Campus;P.G. Department of Physics, Magadh University
关键词: Barium Titanate;    BST;    Ni-Zn ferrite;    composites;    Article;   
来源: National Institute of Science Communication and Information Resources
PDF
【 摘 要 】

Here, we are reporting electrical properties of Barium Titanate and Ni-Zn ferrite magneto-electric composites. Sr substituted barium titanate (BST = 90%) and MnO2 doped nickel zinc ferrite (NZF = 10%) were selected as individual phases for magneto-electric composite. Individual Ba0.9Sr0.1TiO3 and Ni0.8Zn0.2Fe2O4 were prepared separately through solid state reaction route. For structural analysis, the sintered samples subjected to X-ray diffraction reveal a presence of both the ferrite and ferroelectric phase in the composite sample. Dielectric properties were measured as a function of frequency and temperature. Curie temperature for pure BST was observed to be 92 C, whereas in the composite sample, the transition became broader. P-E hysteresis loops were recorded at 20 Hz for all the samples.

【 授权许可】

Unknown   

【 预 览 】
附件列表
Files Size Format View
RO202307160002073ZK.pdf 872KB PDF download
  文献评价指标  
  下载次数:1次 浏览次数:1次