Comparative evaluation of push-out bond strength of single and multiple fiber-reinforced posts cemented with dual-cure resin cement using different adhesive strategies: An in vitro study | |
article | |
Prashant, P Moogi1  Sonawane, Asmita Ashok1  Siddhesh, D Bandekar1  Shirin, P Kshirsagar1  Kalyani, I Ahirrao1  Tryambake, R Pavan1  | |
[1]Department of Conservative Dentistry and Endodontics, Yogita Dental College and Hospital | |
关键词: Dentapreg multiple pin posts; fiber-reinforced posts; push-out bond strength; self-etch; total-etch; | |
DOI : 10.4103/endo.endo_90_22 | |
学科分类:材料科学(综合) | |
来源: Wolters Kluwer Medknow Publications | |
【 摘 要 】
Aims: The aim of the present study was to evaluate and compare the push-out bond strength of single and multiple fiber-reinforced posts cemented with dual-cure resin cement using total-etch and self-etch adhesive systems. Methods: Sixty single-rooted maxillary permanent incisors were decoronated and endodontically treated. Following post space preparations, the roots were divided into four groups (n = 15); Group 1: single fiber-reinforced composite post with the total-etching agent, Group 2: single fiber-reinforced composite post with the self-etching agent, Group 3: multiple pin posts with the total-etching agent, and Group 4: multiple pin posts with the self-etching agent and then cemented using dual-cure resin cement. The samples were then sectioned to obtain approximately 2-mm disks, and a push-out test was performed. Data obtained were statistically analyzed using analysis of variance, post hoc Tukey, and unpaired t-test. Results: The mean push-out bond strength values showed that Group 3 had significantly higher bond strength as compared to the other groups (P < 0.05). Conclusions: Dentapreg multiple pin posts with total-etching agents resulted in higher push-out bond strength as compared to single fiber-reinforced posts and self-etching agents.【 授权许可】