Study on preparation of light oil regenerant and performance of cold recycled mixture | |
article | |
Xiaofeng Huang1  Cheng Xie1  Jiangcai Chen1  Junhui Luo1  Di Wei1  | |
[1] Guangxi Beitou Transportation Maintenance Technology Group Co., Ltd | |
关键词: Road engineering; Reclaimed mixture; Light oil regenerant; Road performance; | |
DOI : 10.1590/1517-7076-RMAT-2023-0101 | |
学科分类:工程和技术(综合) | |
来源: Universidade Federal do Rio de Janeiro * Coordenacao dos Programas de Pos-Graduacao de Engenharia | |
【 摘 要 】
In order to make full use of aged asphalt, a light oil regenerant for cold mixing was prepared in this paper, and the ratio of regenerant and regeneration effect was studied through the performance test of recycled asphalt. The ratio of regenerant was determined by 60 °C kinematic viscosity, mass loss before and after aging, and asphalt three indicators. The thermogravimetric analysis determined the four-component ratio of recycled asphalt, and the mechanical properties of the recycled asphalt mixture were determined by the 15 °C splitting and 20 °C compression tests. Finally, the road performance of the recycled asphalt mixture was analyzed by rutting, low-temperature bending, and dry-wet splitting tests. When the mass ratio of light base oil: plasticizer: stable equilibrium agent: penetrant: the anti-aging agent is 80:20:25:8:5, it has a good regeneration effect. After adding 8% regenerant, the regenerated asphalt is compared with the recycled asphalt. The content of saturates and aromatics increases, and the content of resins and asphaltenes decreases. The four-component content of recycled asphalt is close to that of new asphalt. The mechanical properties test shows that the optimum content of the regenerant is 0.9%. With increased RAP content, the water stability and low-temperature crack resistance are also improved, and the high-temperature stability is reduced. However, it still meets the requirements of the regeneration specification.