Análise mecânica e metalúrgica da união soldada entre um aço inoxidável duplex S32205 com metal de adição de aço inoxidável superaustenítico ER-385-904L
article
Alessandro dos Santos Andrade1  Jorge Luis Braz Medeiros1  Luciano Volcanoglo Biehl1  José de Souza2  Diego de Jesus Pacheco3  Carlos Otávio Damas Martins4 
[1] Universidade Federal do Rio Grande;Fundação Escola Técnica Liberato Salzano da Cunha;Aarhus Universitet;Universidade Federal de Sergipe
关键词: Duplex stainless steel;    Superaustenitic stainless steel;    Welding;   
DOI  :  10.1590/1517-7076-RMAT-2022-0307
学科分类:工程和技术(综合)
来源: Universidade Federal do Rio de Janeiro * Coordenacao dos Programas de Pos-Graduacao de Engenharia
PDF
【 摘 要 】

The welding of dissimilar steels such as duplex and superaustenitic stainless steels is often used in industrial applications. The effect of welding energy on the heat-affected zone (ZTA) and fusion zone (ZF) presents knowledge gaps to be researched in relation to the metallurgical and mechanical properties of these steels. Variations in the application of welding energy can favor the presence of a greater volume of the ferritic or austenitic phases, and in more critical cases, cause the formation of precipitates harmful to corrosion. This work aims to evaluate the metallurgical, mechanical properties and corrosion resistance of dissimilar welding composed of duplex stainless steel S32205, as base metal, and superaustenitic stainless steel as weld metal, verifying the effects on microstructural, sensitization and anisotropies with the application of different heat inputs. In the microstructural analysis, the formation of first phase constituents, such as grain boundary austenite (GBA), witmanstatten austenite (WA), intragranular austenite (IGA) and secondary austenite (γ2) was verified. The microhardness values found were higher than those reported in the literature. In the corrosion tests, in environments with oxidizing chlorides, the samples showed pitting corrosion, with a high loss of mass in the specimens being detected. It is concluded that in the ZTA the metallurgical characteristics were maintained after the variation of the thermal input and in the ZF there was an increase in the loss of mass in the corrosion test in the analyzed samples.