Optical and electronic properties of Si nanoclusters synthesized in inverse micelles

Article

关键词: SILICON CLUSTERS;    POROUS SILICON;    QUANTUM CONFINEMENT;    SURFACE-STATES;    PHOTOLUMINESCENCE;    SEMICONDUCTOR;    LIGHT;    NANOCRYSTALS;    CRYSTALLITES;    ABSORPTION;   

DOI  :  10.1103/PhysRevB.60.2704

来源: SCIE

【 摘 要 】

Highly crystalline, size-selected silicon (Si) nanocrystals in the size range 2-10 nm were,grown in inverse micelles and their optical absorption and phoeoluminescence (PL) properties were studied. High resolution TEM and electron diffraction results show that these nanocrystals retain their cubic diamond structures down to sizes similar to 4 nm in diameter, and optical absorption data suggest that this structure and bulklike properties an retained down to the smallest sizes produced (similar to 1.8 nm diameter containing about 150 Si atoms). High pressure liquid chromatography techniques with on-line optical and electrical diagnostics were developed to purify and separate the clusters into pure, monodisperse populations. The optical absorption revealed features associated with both the indirect and direct band-gap transitions, and these transitions exhibited different quantum confinement effects. The indirect band-gap shifts from 1.1 eV in the bulk to similar to 2.1 eV for nanocrystals similar to 2 nm in diameter and the direct transition at Gamma(Gamma(25)-Gamma(15)) blueshifts by 0.4 eV from its 3.4 eV bulk value over the same size range. Tailorable, visible, room temperature PL in the range 700-350 nm (1.8-3.5 eV) was observed from these nanocrystals. The most intense PL was in the violet region of the spectrum (similar to 365 nm) and is attributed to direct electron-hole recombination. Other less intense PL peaks are attributed to surface state and to indirect band-gap recombination. The results are compared to earlier work on Si clusters grown by other techniques and to the predictions of various model calculations. Currently, the wide variations in the theoretical predictions of the various models along with considerable uncertainties in experimental size determination for clusters less than 3-4 nm, make it difficult to select among competing models. [S0163-1829(99)02328-0].

【 授权许可】

Free