Epitaxy of diamond on Si(100) and surface-roughening-induced crystal misorientation

Article

关键词: 001 SILICON;    GROWTH;    FILMS;    NUCLEATION;    COALESCENCE;    GRAINS;   

DOI  :  10.1103/PhysRevB.64.245413

来源: SCIE

【 摘 要 】

In a recent paper [Phys. Rev. Lett. 84, 3658 (2000)] a direct diamond epitaxy on the silicon substrate is demonstrated not only at the interface formed during the growth process but also at the nucleation sites. Small (001) terraces with dimensions of several atomic distances at the site of nucleation are observed due to the roughening of silicon surface and lead to the grain misorientation, To further improve the understanding of the subject the microstructure and interfaces in diamond films on silicon substrates grown in the stages of the bias-enhanced nucleation (BEN) and the initial crystal growth were studied by means of atomic force microscopy, scanning electron microscopy, and high-resolution transmission electron microscopy. It is showed that the roughness of the wafer starts to increase from the beginning of the BEN and the renucleation on existing crystallites induced by the ion bombardment leading to the loss of epitaxy.

【 授权许可】

Free