Electronic phase diagram of LixCoO2 revisited with potentiostatically deintercalated single crystals

Article

关键词: LITHIUM;    INTERCALATION;    TRANSITION;    COO2;   

DOI  :  10.1103/PhysRevB.85.035120

来源: SCIE

【 摘 要 】

Electronic phase diagram of LixCoO2 has been reexamined using potentiostatically de-intercalated single-crystal samples. Stable phases of x similar to 0.87, 0.72, 0.53, 0.50, 0.43, and 0.33 were found and isolated for physical property studies. A-type and chain-type antiferromagnetic orderings have been suggested from magnetic susceptibility measurement results in x similar to 0.87 and 0.50 below approximately 10 and 200 K, respectively, similar to those found in NaxCoO2 system. There is no Li vacancy superlattice ordering observed at room temperature for the electronically stable phase Li0.72CoO2 as revealed by synchrotron x-ray Laue diffraction. The peculiar magnetic anomaly near similar to 175 K as often found in powder samples of x similar to 0.46-0.78 cannot be isolated through this single-crystal potentiostatic method, which supports the previously proposed explanation to be a surface stabilized phase of significant thermal hysteresis and aging character.

【 授权许可】

Free