Revealing the formation mechanism and band gap tuning of Sb 2 S 3 nanoparticles

Beilstein Journal of Nanotechnology

article

Maximilian Joschko¹  Franck Yvan Fotue Wafo¹  Christina Malsi¹  Danilo Kisić²  Ivana Validžić²  Christina Graf¹ 

[1] Hochschule Darmstadt - University of Applied Sciences;Vinča Institute of Nuclear Sciences, National Institute of the Republic of Serbia, University of Belgrade

关键词: band gap;    kinetics;    nanoparticles;    Sb2S3;    solar cells;   

DOI  :  10.3762/bjnano.12.76

学科分类：环境监测和分析

来源: Beilstein - Institut zur Foerderung der Chemischen Wissenschaften

【 摘 要 】

Sb2S3 is a promising nanomaterial for application in solar cells and in the fields of electronics and optoelectronics. Herein, Sb2S3nanoparticles were prepared via the hot-injection approach. In contrast to earlier work, the reaction temperature was decreased to150 °C so that the reaction was slowed down and could be stopped at defined reaction stages. Thereby, the formation mechanism ofthe nanomaterial and the associated kinetics could be revealed. Based on morphological and structural analyses, it is suggested thatseed particles (type 0) formed immediately after injecting the antimony precursor into the sulfur precursor. These seeds fused toform amorphous nanoparticles (type I) that contained a lower percentage of sulfur than that corresponding to the expected stoichiometric ratio of Sb2S3. The reason for this possibly lies in the formation of an oxygen- or carbon-containing intermediate during theseeding process. Afterward, the type I nanoparticles aggregated into larger amorphous nanoparticles (type II) in a second hierarchical assembly process and formed superordinate structures (type III). This process was followed by the crystallization of theseparticles and a layer-like growth of the crystalline particles by an Ostwald ripening process at the expense of the amorphous particles. It was demonstrated that the kinetic control of the reaction allowed tuning of the optical band gap of the amorphous nanoparticles in the range of 2.2–2.0 eV. On the contrary, the optical band gap of the crystalline particles decreased to a value of 1.7 eV andremained constant when the reaction progressed. Based on the proposed formation mechanism, future syntheses for Sb2S3 particlescan be developed, allowing tuning of the particle properties in a broad range. In this way, the selective use of this material in a widerange of applications will become possible.